Nd: Crystal YAG
Nd: I-YAG (i-Neodimium Doped Yttrium Aluminium Garnet) iye yaqhubeka futhi yaziwa njenge-crystal laser esetshenziswa kakhulu kuma-laser aqinile. Isikhathi esihle se-fluorescence (siphindwe kabili ukwedlula leso seNd: YVO4) kanye nokwenza okuhle kokushisayo, kanye nemvelo enamandla, kwenza i-Nd: i-YAG crystal ilungele kakhulu amandla aphezulu aqhubekayo, amandla aphezulu we-Q-switched kanye nemodi yokusebenza eyodwa.
I-WISOPTIC ihlinzeka ngoNd: Izinduku ze-YAG ezinezici ezilandelayo: amazinga e-doping ahlukene, i-homogeneity ephezulu ye-optical, ukunemba okuphezulu kokucaca, ukubopha okuqondile komgqomo kanye ne-engela yomtshado, ukusikeka okuhlukahlukene okuhlukahlukene, ukumbozwa okuhlukahlukene kokudaya, ukubopha okukhulu komkhawulo.
Xhumana nathi ukuthola isixazululo esihle kakhulu sohlelo lwakho lwe-Nd: amakristalu we-YAG.
Amakhono weWISOPTIC - Nd: YAG
• Izinketho ezahlukahlukene ze-Nd-doping ratio (0.1% ~ 1.3at%)
• Izinketho ezahlukahlukene zezinduku noma ama-slabs (flat, wedig, Brewster, aqokiwe, njll)
• I-homogeneity ephezulu yamehlo
• Ukulungiswa okuphezulu kokusebenza
• Ukuhlanganiswa kwekhwalithi ephezulu, umkhawulo womonakalo omkhulu
• Intengo yokuncintisana kakhulu, ukulethwa okusheshayo
Ukucaciswa Okujwayelekile kwe-WISOPTIC* - Nd: YAG
| Ukulinganisa Okujwayelekile Kwe-Doping | Nd% = 0,1% ~ 1.3at% |
| Ukuzilolonga | <111> noma <100> noma <110> |
| Ukubekezelela Ukubekezela | +/- 0.5 ° |
| Ubukhulu | Ububanzi: 2 ~ 15 mm, Ubude: 3 ~ 220 mm |
| Ukubekezelela Isilinganiso | Ububanzi (± 0.05) × Ubude (± 0.5) mm |
| Qeda umgqomo | Ground nge-400 # grit, noma iphuculiwe |
| I-Flatness | <λ / 10 @ 632.8 nm |
| Ikhwalithi ephezulu | <10/5 [S / D] |
| Ukufana | <10 " |
| I-Perpendicularity | ≤ 5 ' |
| I-Chamfer | 0.15 ± 0.025mm @ 45 ° |
| UkudluliswaKwehlukaniswa Kwangaphambili | <λ / 10 @ 632.8 nm |
| Sula ukuthambisa | > 90% indawo ephakathi nendawo |
| Izilinganiso Zokuqothula | > 30 dB |
| Ukupheka | I-AR-Coating: R <0.10% @ 1064nm |
| Umkhawulo wokulimala kwe-Laser | > 800 MW / cm2 kwe-1064nm, 10ns, 10Hz (i-AR-camera) |
| * Imikhiqizo enesidingo esikhethekile ngesicelo. | |
Izici eziphambili - Nd: YAG
• Ukuthola okuphezulu, umkhawulo ophansi, ukusebenza kahle kakhulu
• Ukusatshalaliswa kwe-Nd okuphelele
• Ukushiswa okukhulu okuphezulu, ukumelana nokushiswa okuphezulu okuphezulu
• I-homogeneity ephezulu, ukuhlanekezela okuphansi
• Ikhwalithi ephezulu yamehlo, ukulahleka kokudlula okuphansi okukodwa (ikakhulukazi nge-1064nm)
• Izinhlobo ezahlukahlukene zokusebenza (CW, pulsed, Q-switched, mode Lock)
Izakhiwo Zomzimba - Nd: YAG
| Ifomula yamakhemikhali | Y3-3xNd3xAl5O12 (x = Nd doping ratio) |
| Isakhiwo se-Crystal | Cubic |
| Ama-Lattice constants | 12.01 Å |
| Ubukhulu | 4,5 g / cm3 |
| Rupture stress | 1.3 ~ 2.6 × 103 kg / cm2 |
| Iphuzu lokuncibilika | 1970 ° C |
| Ubunzima be-Mohs | 8 ~ 8.5 |
| Ukuziphatha okuhle | 14 W / (m · K) @ 20 ° C, 10.5 W / (m · K) @ 100 ° C |
| Ama-coefficients wokwanda kwe-Thermal | 7.8x10-6 / K @ <111>, 7.7x10-6 / K @ <110>, 8.2x10-6 / K @ <100> |
| Ukumelana nokushiswa kokushiswa | 790 W / m |
Izindawo Zokukhanya - Nd: YAG
|
Ukushintshwa kwe-Laser |
4F3/2 → 4Mina11/2 @ 1064 nm |
|
Amandla we-Photon |
1.86 × 10-19 J |
|
Umugqa womugqa wokukhipha |
4.5Å @ 1064 nm |
|
Isigaba esiphakathi esikhutshiwe |
2.7 ~ 8.8x10-19 / cm2 @ Nd% = 1.0at% |
|
Ukulahleka kwama-coefficients |
0.003 / cm @ 1064 nm |
|
Isikhathi se-Fluorescence |
I-230 µs @ 1064 nm |
|
Inkomba ebonakalayo |
1.818 @ 1064 nm |
|
Pump wavelength |
I-807.5 nm |
|
Ibhendi ye-Absorption ku-pump wavelength |
1 nm |
|
Ukukhuphuka kwangaphakathi |
Akuhlukaniswanga |
|
I-birefringence eshisayo |
Phezulu |